1C49

HumiSeal® 1C49 is a moisture curing, high build, VOC-free silicone conformal coating which provides excellent moisture and environmental protection for printed circuit assemblies. HumiSeal® 1C49 is solvent free. The coating demonstrates outstanding flexibility, fluoresces under UV light for ease of inspection and can be repaired. HumiSeal® 1C49 can be cured at room or at elevated temperatures. HumiSeal® 1C49 is MIL-I-46058C qualified, IPC-CC-830 and RoHS Directive 2011/65/EU compliant, and recognized under UL File Number E105698.

button (1)                                     SDS Request

Cleanliness of the substrate is of extreme importance for the successful application of a conformal coating. Surfaces must be free of moisture, dirt, wax, grease, flux residues and all other contaminants. Contamination under the coating could cause problems that may lead to assembly failures.

Brushing
Uniformity of the film depends on component density and operator’s technique.

Dipping
A controlled rate of immersion and withdrawal (5-15 cm/min) will ensure even deposition of the coating and ultimately a uniform film. Blanketing dip tanks with an inert gas such as nitrogen can extend pot life.

Spraying
HumiSeal® 1C49 may be applied using spraying equipment designed for high viscosity coatings. Attempting to apply the material using conventional spray equipment may result in bubbles in the cured HumiSeal® 1C49 coating. When in doubt, test the ability of the spray equipment before applying coating to production boards. Spraying should be done in an environment with adequate ventilation so that the vapour and mist are carried away from the operator. The use of thinner is not required or recommended for HumiSeal® 1C49.

Product Specification

Product Specification
Density, per ASTM D1475 0.97 ± 0.03 g/cm³
Min. Solids Content, % by weight per Fed-Std-141, Meth. 4044 95 %
Viscosity, per Fed-Std-141, Meth. 4287 9000 ± 1500 centipoise
VOC 0 grams/litre
Recommended Coating Thickness 50 – 200 microns
Drying Time to Handle per Fed-Std-141, Meth. 4061 3 – 5 hours
Recommended Curing Conditions 24 hrs @ RT or 20 min @ 76°C*
Time required to Reach Optimum Properties 7 days
Recommended Stripper HumiSeal Stripper 1091
Shelf Life at Room Temperature, DOM 12 months
Thermal Shock, 50 cycles per MIL-I-46058C -65°C to 200°C
Coefficient of Thermal Expansion – TMA 367 ppm /ºC
Glass Transition Temperature – DSC < -65°C
Storage Modulus – DMA 408 MPa @ -40ºC
1.6 MPa @ 25ºC
1.4 MPa @ 80ºC
Tensile, per ASTM D412 30-50 psi
Elongation, per ASTM D412 80-120 %
Build per Dip, per ASTM D823 5 mils
Flammability, per UL94 V-1
Dielectric Withstand Voltage, per MIL-I-46058C >1500 volts
Dielectric Breakdown Voltage, per ASTM D149 7000 volts
Dielectric Constant, at 1MHz and 25°C per ASTM D150-98 2.5
Dissipation Factor, at 1MHz and 25°C per ASTM D150-98 0.01
Insulation Resistance, per MIL-I-46058C 5.0 x 1014 ohms (500TΩ)
Moisture Insulation Resistance, per MIL-I-46058C 1.0 x 1010 ohms (10GΩ)
Fungus Resistance, per ASTM G21 Passes

* Place an open pan of water in the oven during curing